CHEN Rongzhang
,
WANG Luobao
,
WANG Yuping Institute of Aeronautical Materials
,
Beijing
,
PRC.
材料科学技术（英）
The microstructure changed markedly with increasing solution temperature, i.e eutectic γ' phases and coarse primary γ' phase are redissolved continuously into matrix, which was finished at 1250-1260℃, and more and finer γ' phases are reprecipitated. The grain boundary morphology changed gradually to "fine line" form. The dendritic segregation of elements decreased. With raising solution temperature the longitudinal stress-rupture life at high and intermediate temperature were enhanced, but the transversal stress-rupture life at intermediate temperature decreased obviously. The incipient melting temperature of DZ22 alloy was measured to be 1230-1240℃ and may be increased by homogenization at 1150℃. In this paper the principle of determining solution temperature of DS alloys was discussed. It was suggested that the solution temperature of alloy DZ22 selected at 1200-1210℃ is appropri- ate.
关键词:
directional solidification
,
null
,
null
,
null
徐建伟
,
边丽虹
,
薛强
,
曾卫东
钛工业进展
研究了固溶温度对TA19钛合金棒材显微组织和力学性能的影响规律.结果表明:随着固溶温度的升高,等轴α相含量下降较快,大致呈先快后慢的双线性下降变化趋势,而等轴α相尺寸变化较小,大致呈线性下降;β相在固溶过程中发生再结晶,且再结晶晶粒随固溶温度升高而长大.TA19钛合金棒材的抗拉强度和屈服强度随固溶温度的升高而降低,延伸率和断面收缩率基本保持在同一水平上,其强度的变化主要受滑移长度的影响,合金元素分配作用所引起的基体弱化对强度也有一定的作用.
关键词:
TA19钛合金
,
固溶温度
,
显微组织
,
力学性能
万明攀
,
赵永庆
,
曾卫东
,
马瑞
,
边红岩
稀有金属材料与工程
研究了Ti-1300合金经不同温度固溶处理和固溶+时效处理后的组织和性能.结果表明:Ti-1300合金在固溶处理后,随着固溶温度升高,合金的抗拉强度和屈服强度逐渐降低,断面收缩率先升高后降低,断后伸长率有所升高.Ti-1300合金在850℃固溶处理可获得最佳的综合性能.通过固溶和时效处理,Ti-1300合金硬度随着固溶温度的升高而增大.当固溶处理在相变点以下时,β相中时效析出次生αs相较粗大;而固溶处理在相变点以上时,β相中时效析出次生αs相较细小且均匀.
关键词:
固溶温度
,
Ti-1300合金
,
显微组织
,
力学性能
向红亮
,
卢奇敏
,
刘东
,
杨彩萍
材料热处理学报
通过中频感应炉熔炼制备了经济节Ni型铸造双相不锈钢Cr25Mn10Mo4Ni2N,利用OM、XRD、SEM和电化学工作站研究了1000～1150℃温度区间对其显微组织及固溶处理后在人工海水中耐蚀性能的影响.结果表明,固溶温度处于1000 ～1100℃区间时,材料的组织由α、γ及σ相组成.随着固溶温度升高,σ相的形貌由细小岛状向粗大岛状变化,且数量不断减少.当固溶温度升高至1120℃时,σ相完全消失,组织仅由α和γ两相组成.节Ni型双相不锈钢Cr25Mn10Mo4Ni2N经1120固溶时,其腐蚀电流密度最小,电荷转移电阻最大,耐蚀性能最佳;1150℃固溶时,耐蚀性能次之;在1020 ～1100℃温度区间固溶时,随着温度的升高σ相含量减少,材料耐蚀性能越好.
关键词:
节Ni型铸造双相不锈钢
,
固溶温度
,
σ相
,
耐蚀性能
罗峥
,
魏衍广
,
陶海明
,
崔雪飞
,
陈海珊
材料导报
研究了固溶温度对Ti-5Mo-5V-2Cr-3Al钛合金棒材显微组织和力学性能的影响.结果表明,钛合金固溶处理温度在相变点以下,空冷后,显微组织由β相、初生α相以及次生α相组成.随着固溶温度的升高,显微组织中β相晶粒尺寸增大,晶界α相厚度减小,产生有序化现象,而次生α相数量和尺寸减小,使合金的强度降低,塑性升高,但固溶处理温度为800℃时,网状晶界α相使塑性迅速下降;当固溶处理温度在相变点以上,Ti-5Mo-5V-2Cr-3Al钛合金重新形核并长大,随着固溶温度的升高,β相晶粒尺寸增大,初生α相数量减少,强度和塑性都下降,过冷β相晶粒发生应力诱发马氏体现象.
关键词:
Ti-5Mo-5V-2Cr-3Al钛合金
,
固溶温度
,
力学性能
,
显微组织
陶海明
,
魏衍广
,
罗峥
,
崔雪飞
,
陈海珊
材料导报
doi:10.11896/j.issn.1005-023X.2014.16.026
对Ti-5Mo-5V-2Cr-3Al钛合金φ10 mm棒材在不同固溶温度下的拉伸断口形貌进行分析,并研究了断口形貌特征与力学性能之间的关系.结果表明:按照传统的断口分析理论,该材料随着固溶温度升高,塑性下降,实际测试结果却相反,该材料随固溶温度升高,在相变点以下,塑性缓慢升高,在相变点以上,塑性迅速增大;该材料的力学性能受相组成的影响,β相含量越多,棒材的拉伸强度降低,塑性升高;当固溶温度为840℃时,该材料拉伸后的宏观断口平直光滑,微观断口出现尺寸约40μm形状规则的β晶粒,棒材塑性较好.
关键词:
Ti-5Mo-5V-2Cr-3Al钛合金
,
断口分析理论
,
固溶温度
,
塑性
李红英
,
刘洋
,
胡继东
,
武岳
材料热处理学报
采用扫描电镜（SEM）、X射线衍射（XRD）和力学性能测试等手段研究了固溶处理对ZA27合金组织和性能的影响。在300～380℃范围,合金经不同温度固溶处理1 h,水淬后进行相同的时效（160℃×8 h）处理。分析了在不同温度固溶处理的淬火态和时效态合金的显微组织及力学性能。结果表明,在365℃固溶处理能够使溶质原子充分溶入基体,时效析出相数量多、尺寸小、分布均匀,时效强化效果最好。ZA27合金的优选固溶工艺为365℃×1 h。
关键词:
ZA27合金
,
固溶温度
,
组织
,
性能
,
析出相
李红英
,
王晓峰
,
赵延阔
,
曾翠婷
,
张建飞
材料热处理学报
研究了固溶温度对一种新型Al-Cu-Li系合金(2A97铝合金)组织性能的影响.在460～540℃,合金经不同温度固溶处理,水淬后进行相同的时效(165℃×48 h)处理.分析了在不同温度固溶处理的淬火态和时效态合金的显微组织、时效态合金的断口形貌.结果表明:在520℃圃溶处理能够使合金充分固溶,时效后有较细小均匀分布的析出相和较多的析出量,时效强化效果最好.
关键词:
固溶温度
,
2A97铝合金
,
组织
,
性能
,
析出相
梁明岗
,
文九巴
,
贺俊光
,
程丹丹
腐蚀与防护
铝基阳极合金是一种有发展前途的电池用阳极材料,采用开路电位、极化曲线、电化学阻抗谱和恒电流放电曲线等测试方法,研究了电解液温度对铝阳极合金在4 mol·L-1 NaOH溶液中电化学性能的影响.结果表明,随着电解液温度的升高,铝阳极合金的活化性能增强,其开路电位和工作电位明显负移,但合金的自腐蚀析氢速率增大.当温度为40℃时,合金表现出较好的综合性能和均匀的腐蚀形貌.
关键词:
电解液温度
,
铝阳极合金
,
组织
,
电化学性能
魏衍广
,
陶海明
,
陈海珊
稀有金属
doi:10.3969/j.issn.0258-7076.2010.01.002
研究了固溶温度对TB10(Ti-5Mo-5V-2Cr-3Al)钛合金在热处理过程中力学性能变化规律.结果表明:当TB10钛合金在740~840℃之间固溶,并在520℃时效时,在相变点以下固溶,随着同溶温度的升高,材料的强度降低、塑性升高,但在800℃时网状晶界α相恶化了材料的塑性,在相变点以上固溶时,材料的强度和塑性随着固溶温度的升高而下降;时效后的TB10钛合金随着固溶温度升高,材料的强度升高、塑性下降;当固溶温度为740℃时,时效态的材料强度和塑性比固溶态略有升高,固溶温度越高,时效强化效果越显著,时效态材料的塑性比固溶态的低,但在800℃时由于晶界α相的网状被破坏使时效态材料的塑性比固溶态的高.
关键词:
TB10钛合金
,
固溶温度
,
力学性能
,
显微组织